Taulman Nylon 230 - 1Kg
Taulman Nylon 230 - 1Kg
Nylon 230 is the first nylon filament to be processed at 230 °C or lower. This is a lower temperature than any other nylon filament for your FFF/FDM-3D printer. With the launch of Nylon 230 from Taulman 3D, you can now process nylon in your PLA or ABS 3D printer with low temperature. Add high strength nylon to your list of workable materials. In addition, Nylon 230 adheres to BlueTape (painter's masking tape) and even better to "buildTak" type surfaces and various PVA glues/glue sticks.
- 3D printing at 230 °C
- Use a closed build chamber for best adhesion
- Adheres to PVA glue/glue sticks
Couldn't load pickup availability
Share
Taulman Nylon 230
Nylon 230 is the first nylon filament to be processed at 230°C or lower. This is a lower temperature than any other nylon filament for your FFF/FDM-3D printer. With the launch of Nylon 230 from Taulman3D, you can now process nylon in your PLA or ABS 3D printer with low temperature. Add high-strength nylon to your list of machinable materials. In addition, Nylon 230 adheres to BlueTape (painter's masking tape) and even better to "buildTak" type surfaces and various PVA glues/glue sticks.
Material properties:
- 3D printing at 230 °C
- Nylon 230 attaches to BlueTape
- Used built-in for best adhesion
- Adheres to PVA glue/glue sticks
Buy Taulman Nylon 230 if you are looking for a strong and reliable filament wire for your FFF or FDM 3D printer.
Technical Specifications
|
Basic Information |
|
|
Filament type |
P.A |
|
Diameter |
1.75 mm |
|
Tolerance |
0.05 mm |
|
Weight |
1.00 kg |
|
Length |
329 m |
|
Paint |
clear transparent |
|
Paint |
transparent |
|
|
|
|
Parameters for printing |
|
|
Recommended printing temperature Min |
228 ºC |
|
Recommended printing temperature Max |
235 ºC |
|
Recommended pressure bed temperature Max |
55 ºC |
|
Recommended Indentation Min |
3 mm |
|
Recommended indentation Max |
4 mm |
|
Generally |
|
|
Specific gravity |
1,263 |
|
Traction force |
|
|
Tensile strength |
34 MPa |
|
Extension |
|
|
Elongation when stretching |
417% |
|
Bendability |
|
|
Flexural modulus |
73 |